Triune Chemicals and Materials Co LTD.


* * *


1. ()
Bisphenol-A Type Epoxy Resin



1.1. ,
Standard liquid Type


,
,
180-250. ,
, , , ,
.

This series of products, coming from the reaction of Bisphenol A and Epichlorohydrin
(ECH) with different ratio, EEW are controlled between 180-250, they can be widely
used in all applications like Coatings, Adhesive, Casting, Composite, Civil Engineering
and Electric and electronics fields.


ITEM

EEW
(g/eg)

VISCOSITY
(cps/25C)

COLOR
(APHA)

Hy-Cl, PPM

ECH RESIDUE
PPM
,%
VOLATILE (%)
1 2 3 4 5 6 7
LE826 180-190 8000-11000 30 500 5 0,1
LE828 185-195 12000-15000 30 500 5 0,1
LE828LV 180-190 9000-12000 30 - - -
LE828S 184-194 12000-16000 30 500 5 0,1
LE834 230-270 21000-25000 30 500 - 0,5
LE836 300-330 X-Z2 50 - - -


1.2.
Solution & Blends Bisphenol-A Epoxy Resins


ITEM

EEW
(g/eg)

VISCOSITY mPa.s@25 C

COLOR
(Pt-Co) <
1 2 3 4
SLE828-80 180-190 150-1200 1#
SLE834-85 230-270 1800-5000 1#
SLE1001-75 450-500 8000-15000 1#
BLE514 190-210 600-1200 1#
BLE515 180-195 600-1200 1#


1.3. ( )
Solid Epoxy Resin (Indirect method)

,
,

- ,

- ,

- ,

- .

,
.
( 1001)
.

,
, , ,
.

We export full range of solid epoxy resins which can be used in different applications, such as

-anticorrosive paints,

-can coatings,

-powder coatings,

-industrial paints and so on.

We have different types of solid epoxy resins,made by direct and indirect model of production.
Indirect method (Series 1001) posess excellent quality of application film surface and low colour index.

Direct model epoxy resin can be used for industrial and protective coatings, where decorative
properties are less important than functionality, at same time provide cost saving effect.



ITEM

EEW
(g/eg)

SOFTENING POINT(Ѱ)

COLOR <

ORGANIC CHLORIDE
eg/100g

INORGANIC CHLORIDE
eg/100g
,%
VOLATILE (%)


COMMENTS
1 2 3 4 5 6 7 8
SE1001 450-500 65-75 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1001LH 450-500 65-75 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1001HH 475-500 75-85 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1002 600-700 81-91 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1002HH 650-700 87-97 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1003 700-900 90-96 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1003LH 740-800 98-104 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1003HH 780-850 96-107 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1004 800-1000 96-105 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1007 1300-1700 117-127 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1007H 1500-1800 117-127 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1009 1800-2500 130-145 1 <0,0023 <0,0006 <0,1
Clear granule solid resin
SE1009H 2300-3500 130-150 1 <0,0023 <0,0006 <0,1
Clear granule solid resin


1.4. ( )
Solid Epoxy Resin (Direct method)


ITEM

EEW
(g/eg)

SOFTENING POINT(Ѱ)

COLOR <

ORGANIC CHLORIDE
eg/100g

INORGANIC CHLORIDE
eg/100g
,%
VOLATILE (%)


COMMENTS
1 2 3 4 5 6 7 8
SE201 455-550 64-76 1 <0,0003 <0,0005 <0,5
Clear granule solid resin
SE202 600-700 75-82 1 <0,0003 <0,0005 <0,5
Clear granule solid resin
SE203 670-710 89-94 1 <0,0003 <0,0005 <0,5
Clear granule solid resin
SE204 700-900 90-96 1 <0,0003 <0,0005 <0,5
Clear granule solid resin
SE207 1700-2500 115-135 1 <0,0003 <0,0005 <0,5
Clear granule solid resin
SE209 700-900 90-96 1 <0,0003 <0,0005 <0,5
Clear granule solid resin


* * *


2. F ()
Bisphenol-F Type Epoxy Resin



2.1. ,
Standard liquid Type



ITEM

EEW
(g/eg)

VISCOSITY
(cps/25C)

HYDROLYZABLE CHLORIDE, PPM <

WATER
PPM

COLOR
(Pt-Co) <
1 2 3 4 5 6
FE870 160-180 2000-5500 1000 750 200#


* * *


3.
Flame retardant epoxy resin



3.1.
Brominated Epoxy Resin




ITEM

EEW
(g/eg)

VISCOSITY
(cps/25C)

SOLVENT TYPE
(%)
BR.CONTENT
(wt.%) <

COLOR
(Pt-Co) <
1 2 3 4 5 6
BE450A80 410-440 800-1800 18-21 3
BE460A80 450-475 500-1500 19-22 3


* * *


4.
Novolac Epoxy Resin



4.1. .
Phenol Novolac Type Epoxy Resin




ITEM

EEW
(g/eg)

VISCOSITY
(cps/25C)

HYDROLYZABLE CHLORIDE, PPM <

VOLATILE
% <

COLOR
(G)


COMMENTS
1 2 3 4 5 6 7
NE438 172-182 20000-35000 1200 0,3 250#
A semi-solid reaction product


* * *


5. .
Reactive Diluents




ITEM

EEW
(g/eg)

VISCOSITY
(mPa.s@25C)

COLOR
(Pt-Co)

Hy-Cl, eg/100g <

BILLING RANGE
C,>

INORGANIC CHLORIDE
eg/100g

MOISTURE
%<


MEMO
1 2 3 4 5 6 7 8 9
BGE 130-140 5-10 1 0,02 0,005 120 -
Butyl Glycidyl ether
BZGE 230-250 5-12 2 0,02 0,005 180 -
Benzyl Glycidyl ether
CGE 182-222 5-15 2 0,02 0,005 - 0,1 -
o-cresol Glycidyl ether
BDGE 130-170 25-30 1 0,02 0,005 - 0,1 1,4
1,4 butanediol Glycidyl ether
NPDGE 130-145 15-20 1 0,02 0,005 150 -
Diglycidyl ether of neopentan glicol
AGE 270-290 15-20 1 0,02 0,005 - 0,1 12-14
C12-C14 alkyl Glycidyl ether
HDGE 153-162 10-30 1 0,02 0,005 - 0,1 1,6
1,6 hexandiol Diglycidyl ether


* * *


5. . .
Standard type of epoxy vinyl ester resin



VER818 . - , , , . . .

VER818 series resins are the recognized standard for epoxy vinyl ester resins. They are based on Bisphenol-A epoxy resin, and they provide resistance to a wide range of acids, alkalis, bleaches and solvents for use in many chemical processing applications. They offer excellent toughness and fatigue resistance.


ITEM

PROPERTIES OF LIQUID RESIN

PHYSICAL PROPERTIES CURED CASTING
¨
SOLID CONTENT (%)

VISCOSITY (cps, 25 C)

SPECIFIC GRAVITY
()
SHELF LIFE (months,
25 C)

TENSILE STRENGTH (psi)
(105/2)
TESILE MODULUS
, %
TENSELE ELONGATION AT BREAK, %
()
FLEXURAL STENGTH (psi)
(105/2)
FLEXURAL MODULUS

HEAT DISTORTION TEMPERATURE
ڨ
VOLUME SHRINKAGE %
¨
BARCOL HARDNESS
1 2 3 4 5 6 7 8 9 10 11 12 13
VER818-45 55 450 1,04 9 12000 4,9 5,0-6,0 20000 5,0 108 C 7,75 34
VER818-350 55 350 1,04 9 12500 5,0 5,0-6,0 20000 4,85 110 C 7,5 34


6.
Novolac type of epoxy vinyl ester resin



VER878 - , . , , . , .

VER878 series resins are epoxy Novolac-based vinyl ester resins designed to provide exceptional thermal and chemical resistance properties. They offer high resistance to solvents, acids and oxidizing substances such as chlorine. They also offer high retention of strength and toughness at elevated temperatures, making them the resins of choice for flue gas applications.


ITEM

PROPERTIES OF LIQUID RESIN

PHYSICAL PROPERTIES CURED CASTING
¨
SOLID CONTENT (%)

VISCOSITY (cps, 25 C)

SPECIFIC GRAVITY
()
SHELF LIFE (months,
25 C)

TENSILE STRENGTH (psi)
(105/2)
TESILE MODULUS
, %
TENSELE ELONGATION AT BREAK, %
()
FLEXURAL STENGTH (psi)
(105/2)
FLEXURAL MODULUS

HEAT DISTORTION TEMPERATURE
ڨ
VOLUME SHRINKAGE %
¨
BARCOL HARDNESS
1 2 3 4 5 6 7 8 9 10 11 12 13
VER878-300 61 430 1,06 6 12000 5,15 2,5-4,0 18500 5,40 150 C 8,5 43
VER878-400 65 400 1,07 3 - 5 12000 5,15 2,2-2,8 18500 5,65 165 C 9 43
VER878H-400 71,5 750 1,08 3-5 10000 5,45 1,5-2,5 15500 5,85 210 C 9 52


6.
Brominated type of epoxy vinyl ester resin



VER858 . . , .

VER858 series resins are Brominated epoxy vinyl ester resins that offer a high degree of fire retardance. They are very resistant to chemical attack by chlorine and bleach environments. Their bromine content makes them tougher and more fatigue resistant than standard epoxy vinyl ester resins.


ITEM

PROPERTIES OF LIQUID RESIN

PHYSICAL PROPERTIES CURED CASTING
¨
SOLID CONTENT (%)

VISCOSITY (cps, 25 C)

SPECIFIC GRAVITY
()
SHELF LIFE (months,
25 C)

TENSILE STRENGTH (psi)
(105/2)
TESILE MODULUS
, %
TENSELE ELONGATION AT BREAK, %
()
FLEXURAL STENGTH (psi)
(105/2)
FLEXURAL MODULUS

HEAT DISTORTION TEMPERATURE
ڨ
VOLUME SHRINKAGE %
¨
BARCOL HARDNESS
1 2 3 4 5 6 7 8 9 10 11 12 13
VER858-40 58 380 1,15 6 12000 5,2 4,5-5,5 17500 5,2 106 C 7,75 40
VER858-350 65 300-450 1,15 9 12000 4,5 5,0-6,0 20000 4,95 116 C 7,5 35
VER858N 62 350 1,15 4 11000 5,15 5,2-5,7 19000 5,4 130 C 8,5 42


6.
Modified type of epoxy vinyl ester resin



VER , , . .

VER Modifiled series resin is a kind VER based on Bisphenol-A epoxy vinyl ester resin and moidifled by Novolac or Elastomers that offers very high toughness, impact- and fatigue- resistance, and excellent adhesion. It is the resin of choice for demanding structural applications and as a primer for chemically resistant FRP linings.


ITEM

PROPERTIES OF LIQUID RESIN

PHYSICAL PROPERTIES CURED CASTING
¨
SOLID CONTENT (%)

VISCOSITY (cps, 25 C)

SPECIFIC GRAVITY
()
SHELF LIFE (months,
25 C)

TENSILE STRENGTH (psi)
(105/2)
TESILE MODULUS
, %
TENSELE ELONGATION AT BREAK, %
()
FLEXURAL STENGTH (psi)
(105/2)
FLEXURAL MODULUS

HEAT DISTORTION TEMPERATURE
ڨ
VOLUME SHRINKAGE %
¨
BARCOL HARDNESS
1 2 3 4 5 6 7 8 9 10 11 12 13
VER878-400 71,5 750 1,08 3 - 5 10000 5,45 1,5-2,5 15500 5,85 210 C 9 52
VER878H-400 71,5 750 1,08 3 - 5 10000 5,45 1,5-2,5 15500 5,85 210 C 9 52
VER898 45 400 1,02 9 10000 4,75 6,0-9,0 16000 4,55 85 C 8,0 32
VER898-1 57 400 - 6 9594 - 12 18406 4,5 95 C - 32